First principle calculations of frictional forces for realistic systems are gener-
ally impossible, since friction is an interfacial property, often determined by the
last few uncontrolled monolayers of atoms or molecules at the interface. In dia-
mond, a huge friction results between two clean surfaces in ultra high vacuum,
because of the strong interaction between the surface dangling bonds. However,
saturation of these bonds by a hydrogen monolayer (as they generally are in
reality) leads to extremely low friction. Since most surfaces of practical use are
covered by several monolayers of contaminant molecules of unknown composi-
tion, a quantitative prediction of sliding friction coefficients is not possible. An
exception to this may be rubber friction on rough surfaces.
Rubber friction is of great practical importance, e.g., in the context of tires,
wiper blades, conveyor belts and rubber seals. Rubber friction on smooth sub-
strates, e.g., on smooth glass surfaces, has two contributions, adhesive (surface)
and hysteretic (bulk). The former results from the attractive forces between the
rubber surface and the substrate. Surface forces are often dominated by weak
attractive van der Waals interactions. For very smooth substrates, because of
the low elastic moduli of rubber-like materials, this weak attraction may result
in a nearly complete contact at the interface, even when the applied squeezing
force is very small. The result is the large sliding friction force usually observed.
For rough surfaces, however, the adhesive contribution will be much smaller be-
cause of the small contact area. The actual contact area between a tire and
a road surface, for example, is typically around 1% of the nominal footprint
contact area, i.e., of order of 1 cm
2
for the tire of a family car. Under these
conditions, bulk (hysteretic) friction should prevail. For example, the extreme
temperature-dependence of tire-road friction reflects the strong temperature de-
pendence of the viscoelastic bulk properties of rubber.
The main contribution to rubber friction when a rubber block slides on a
rough substrate, i.e., a tire on a road surface, is the viscoelastic energy dissipa-
tion in the surface region of the rubber. These result from the pulsating forces
acting on the rubber surface from the substrate asperities (see Figure 1). Re-
cently we developed a theory that describes this dissipation process accurately,
and also predicts the velocity dependence (and the time-history dependence)
of the rubber friction coefficient. The results depend only on the (complex)
viscoelastic modulus E(ω) of the rubber and the substrate surface roughness
power spectra C(q), and agrees well with experiment.